Polyester Resin E Glass Fiberglass Fabric Tape For Armatures Transformers

Categories Fiberglass Banding Tape
Brand Name: Jiangnan
Model Number: H200
Certification: ISO9001:2015
Place of Origin: CHINA
MOQ: 500 Meters
Price: Negotiable
Payment Terms: L/C, D/A, D/P, T/T, Western Union
Supply Ability: 10000 Square Meters per day
Delivery Time: 14 Days after the Payment
Packaging Details: Carton Box
Product Name: Polyeste Impregnated Insulation Binding Tape
Thicknee: 0.3mm
Thermal Class: H
Loss of Weight at Calcination: 27%
Soluble Resin Content: More Than 90%
Tensile Strength Before Curing: More Than 1000 N/cm
Storage Time: 6Months
Materials: continuous,twisted or untwisted E-glass Yarn
  • Haven't found right suppliers
  • Our buyer assistants can help you find the most suitable, 100% reliable suppliers from China.
  • And this service is free of charge.
  • we have buyer assistants who speak English, French, Spanish......and we are ready to help you anytime!
  • Submit Buying Request
    • Product Details
    • Company Profile

    Polyester Resin E Glass Fiberglass Fabric Tape For Armatures Transformers

    0.3mm Thickness Insulation Binding Tape Polyester Resin Impregnated Fiberglass Web Banding Tape


    1. Introduction:

    Polyglass banding tapes consists of high-strength glass yarns laid parallel, impregnated with special high-temperature thermosetting polyester resin. During cure, the resin flows and fills the voids and air spaces to produce a homogeneous laminate with a smooth resin surface.



    2. Specification



    Type
    (mm)
    Thickness
    (mm)
    Tolerance
    (mm)
    Width
    (mm)
    Tolerance

    Put up

    H200


    F150

    0.20±0.0310±1
    pancake or spool
    15±1.5
    0.30±0.03
    20.25.30.50.60±2



    3. Polyester Resin Fiberglass Banding Tape Transportation


    Banding tape requires special and rapid transportation arrangements. Mutual consultation is suggested for appropriateness depending on the transit period, available modes, handling, etc. Considering the sensitivity of banding tape, the buyer needs to quickly take delivery of the consignment and store it suitably

    4. Storage stability

    The banding tape should be stored in a low temperature environment. When using, the tape should be restored to the surrounding environment. Outside the use time, it is best to put it in a plastic cover and seal it to keep it clean and prevent moisture from condensing on the product at low temperatures.



    5. Properties


    Item

    Unit

    Figure

    Type
    H200F150-

    Thermal class
    H(200℃)F(155℃)

    Volatile content
    %≤2

    Loss of weight at calcination
    %26±2

    Soluble resin content
    %≥90

    Tensile strength before curing
    N/cm0.20mm≥1200≥1000
    0.30mm≥2000≥1500

    Maximum pull while banding
    N/cm0.20mm≥600≥500
    0.30mm≥1000≥800

    Tensile strength of ringlike sample at room temperature after curing
    Mpa20℃
    ≥1000≥900

    Tensile strength of ringlike sample at working temperature after curing
    Mpa200℃155℃
    ≥700≥560

    Proof tracking index
    V≥500

    Arc resistance
    S≥160

    Dielectric strength
    KV/mm≥12

    Thermosetting
    OK

    Loss of tensile strength after soaked in oil
    %≤10

    6. Features:


    Thermal class F and thermal class H banding tape

    Banding tape is available in thermal class F (155°C) and thermal class H (200ºC).

    • High thermal resistance of up to 200ºC; short period of heating up to 260ºC may be tolerated, whereas solder may melt on steel wires
    • Very high arc resistance, thereby minimizing the possibility of 'flash over' which has often been a problem with steel bands
    • Resistant to humidity and corrosion
    • Smooth cured surface on application of banding tape reduces dirt adhesion, which might otherwise lead to tracking failure
    • Non-conducting material, hence eliminates insulation as required under steel banding
    • Prevents lashing banding tape bands, eliminating the extreme damage caused by lashing wires and lifting armature coils experienced when steel bands break

    7. Application fields:

    As a winding restraint on traction armatures, generators, other rotating machines and transformer cores

    Applications where high tensile strength and insulating properties of the product can be made use of



    0.2 0.3mm C Epoxy Resin Impregnated Mesh Polyester Fiberglass Banding Tape 0 0.2 0.3mm C Epoxy Resin Impregnated Mesh Polyester Fiberglass Banding Tape 1 0.2 0.3mm C Epoxy Resin Impregnated Mesh Polyester Fiberglass Banding Tape 2
    Rotor banding Large-transformer banding Transformer banding

    Quality Polyester Resin E Glass Fiberglass Fabric Tape For Armatures Transformers for sale
    Send your message to this supplier
     
    *From:
    *To: Changshu Jiangnan Glass Fiber Co., Ltd.
    *Subject:
    *Message:
    Characters Remaining: (0/3000)
     
    Inquiry Cart 0